Élaboration et caractérisation de nouveaux matériaux ferriélectriques ou pyroélectriques de type BaAl2O4 - TEL - Thèses en ligne Accéder directement au contenu
Thèse Année : 1993

Preparation and characteristics of new ferrielectric or pyroelectric materials of the BaAl2O4 family

Élaboration et caractérisation de nouveaux matériaux ferriélectriques ou pyroélectriques de type BaAl2O4

Résumé

New materials based on BaAl2O4 and BaZnGeO4 have been characterized. BaAl2O4 and the derived phases are ferrielectric: the spontaneous polarization has two components with opposite directions and different intensities. A model has been proposed to justify the appearance of a non-stoichiometric phase derived from BaAl2O4.BaZnGeO4 is pyroelectric at 300K; five phase transitions were highlighted. BaZnGeO4 ceramics polarize spontaneously during heat treatment due to the piezoelectric nature of the material.
De nouveaux matériaux à base de BaAl2O4 et BaZnGeO4 ont été caractérisés. BaAl2O4 et les phases dérivées sont ferriélectriques: la polarisation spontanée possède deux composantes de sens opposes et d'intensités différentes. Un modèle a été propose pour justifier l'apparition d' une phase non stoechiométrique dérivée de BaAl2O4.BaZnGeO4 est pyroélectrique a 300K; cinq transitions de phase ont été mises en évidence. Les céramiques de BaZnGeO4 se polarisent spontanément au cours du traitement thermique en raison du caractère piezoélectrique du matériau.
Fichier principal
Vignette du fichier
T9307.pdf (20.93 Mo) Télécharger le fichier

Dates et versions

tel-00136415 , version 1 (13-03-2007)

Identifiants

  • HAL Id : tel-00136415 , version 1

Citer

Sui-Yang Huang. Élaboration et caractérisation de nouveaux matériaux ferriélectriques ou pyroélectriques de type BaAl2O4. Matériaux. Université Sciences et Technologies - Bordeaux I, 1993. Français. ⟨NNT : 1993BOR10568⟩. ⟨tel-00136415⟩

Collections

CNRS LCS
185 Consultations
70 Téléchargements

Partager

Gmail Facebook X LinkedIn More