Pure chromium thermal oxidation in controlled atmosphere : chromia semiconducting and structural properties - Archive ouverte HAL Access content directly
Theses Year : 2018

Pure chromium thermal oxidation in controlled atmosphere : chromia semiconducting and structural properties

Oxydation thermique du chrome pur en atmosphère contrôlée : propriétés semiconductrices et structurales de la chromine

(1)
1

Abstract

The chemical durability of the metal alloy results in particular from the nature of point defects providing transport through the oxidation film formed on the surface. Models oxide layers, grown by thermal oxidation and Alomic Layer Deposition, will be studied by photoelectrochemistry. This will provide us information about the semiconductive properties of the oxide, determined by the point defect in the oxide layer, and should allow us a better understanding of the formation mechanism of these oxide.
La durabilité chimique des alliages métalliques résulte notamment de la nature des défauts ponctuels assurant le transport au travers du film d’oxydation formé en surface. L'élaboration de couches d'oxyde modèles par oxydation thermique en pression contrôlée et ALD (Atomic Layer Deposition) et l'étude de leurs propriétés semi conductrices (conditionnées par la nature des défauts ponctuels) devrait permettre une meilleure compréhension des mécanismes de formation de ces couches d'oxyde.
Fichier principal
Vignette du fichier
PARSA_2018_diffusion.pdf (11.83 Mo) Télécharger le fichier
Origin : Version validated by the jury (STAR)

Dates and versions

tel-02050481 , version 1 (27-02-2019)

Identifiers

  • HAL Id : tel-02050481 , version 1

Cite

Yohan Parsa. Oxydation thermique du chrome pur en atmosphère contrôlée : propriétés semiconductrices et structurales de la chromine. Matériaux. Université Grenoble Alpes, 2018. Français. ⟨NNT : 2018GREAI081⟩. ⟨tel-02050481⟩
234 View
494 Download

Share

Gmail Facebook Twitter LinkedIn More