The mechanical surface treatments confer better local mechanical properties against wear or fatigue service conditions. In the case of impact-based treatments, the material is exposed to repeated mechanical loadings, producing a severe plastic deformation in the near-surface. It leads to a local and progressive refinement of the microstructure into the affected zone, commonly known as Tribologically Transformed Surface (TTS). For this project, two mechanical surface treatments are used in a model material (pure α-iron): (i) shot-peening and (ii) micro-percussion.The resulting surfaces are characterized by a mechanical property gradient in-depth as a consequence of the microstructural transformation over a few tens of microns. Nowadays, it is well-known that this rise of local mechanical properties could improve the service lifetime of materials. However, a simple micro-hardness test is not quite enough to quantify precisely the engendered variation of mechanical properties and understand the influence of several microstructural effects. For this purpose, two micro-mechanical tests are considered: (i) nano-indentation and (ii) in situ micro-pillar compression.The main issue of this work is to characterize the mechanically-induced transformed surfaces and correlate the mechanical properties gradients with the local microstructural evolutions. Indeed, three main goals are considered: (i) quantify the mechanical and microstructural gradients induced by the surface treatments (shot-peening and micro-percussion), (ii) correlate the results obtained by the means of both mechanical tests (nano-indentation and micro-pillar compression) and finally (iii) investigate the influence of several microstructural effects related with the graded strengthening of hyper-deformed surfaces.