The analyses presented in this dissertation deal with damage and failure of heterogeneous materials. The main degradation mechanism is cracking at the lowest level. A probabilistic approach constitutes a useful tool. Brittle materials (such as ceramics, SG cast iron under cyclic loadings) or quasi-brittle materials (e.g., impacted ceramics, fiber-reinforced ceramics, cementitious matrices reinforced by short or continuous fibers) are concerned. The dialogue between different scales is used to build models predicting darnage and failure. On the other hand, different identification strategies are developed to identify the material parameters.
Les analyses présentées dans ce mémoire portent sur l'endommagement et la rupture de matériaux hétérogènes. Le mécanisme principal de dégradation est la fissuration à l'échelle la plus petite. Une approche probabiliste s'avère être un outil efficace. Ceci concerne des matériaux à comportement fragile (céramiques, fontes GS sous sollicitation cyclique) ou quasi-fragile (céramiques monolithiques impactées ou renforcées par des fibres longues, ciments renforcés par des fibres longues ou courtes). Le dialogue entre les différentes échelles a d'une part permis de construire des modèles de prévision de l'endommagement et de la rupture. D'autre part, diverses stratégies d'identification des paramètres du matériau ont été mises en oeuvre.