Fonctionnalisation d’électrodes de silicium nanostructuré par couches nanométriques de diélectrique par ALD : une protection active versatile pour des micro-supercondensateurs ultra-stables en milieux aqueux - TEL - Thèses en ligne Accéder directement au contenu
Thèse Année : 2020

Fonctionalization of nanosctructured silicon electrodes by nano-metric dielectric layers deposited by ALD : an effective and adaptable protection for ultra-stable micro-supercapacitors in aqueous media

Fonctionnalisation d’électrodes de silicium nanostructuré par couches nanométriques de diélectrique par ALD : une protection active versatile pour des micro-supercondensateurs ultra-stables en milieux aqueux

Résumé

In recent years, significant attention has been paid to the development of micro-devices as innovative energy storage solutions. For instance micro-sensor networks such as sensors actuators or implantable medical devices require power densities and cyclability that are several orders of magnitude higher than those of conventional Lithium-Ion batteries. For such applications, Microsupercapacitors (MSCs), a developing novel class of micro/nanoscale power source are rising alternatives, and their integration “on-chip” could allow significant innovations to emerge.1 Therefore, a great deal of attention has been focused on MSCs, for which large series of nanostructured active materials have been developed. Following this trend, we have demonstrated through comprehensive investigations the interest of silicon nanostructures grown by Chemical Vapor Deposition (CVD) as electrodes materials for MSCs using ionic liquid electrolytes. The fine morphological tuning of the nanostructure allowed by the bottom-up approach enables specific designs of electrode architectures, with a considerable leeway compared to other techniques. Such latitude allows optimising porosity and ionic and electronic pathways while keeping robust mechanical and thermal performances, depending on the target application. Nanostructures such as SiNWs and SiNTrs have displayed excellent electrochemical performances being stable over more than 1 million cycles of galvanostatic charge/discharge under a 4 V wide electrochemical windows in EMITFSI ionic liquid, with large power densities of 10 mW.cm-2 and good capacitance values of 0.5 mF.cm-2 at high current density of 0.5 mA.cm-2. However a major silicon weakness which was still hindering its use with aqueous electrolytes is the native uncontrolled growth of silica when subjected to ambient atmosphere. In this thesis we have developed and investigated a highly conformal passivation coating of a nanometric high-k dielectric layer of Al2O3 based on the rising Atomic Layer Deposition (ALD) technique. ALD has proven to allow a nanometric thickness control of the deposited layer while being highly conformal and covering. Moreover, as discusses in this manuscript the protective alumina layer enables the use of aqueous electrolytes for nanostructured Si based MSCs, which significantly increases the specific power of the devices up to 200 mW.cm-2 at 0.5 mA.cm-2 while keeping the capacitance performances at 0.5 mF.cm-2. Furthermore the system is remarkably able to retain 99% of its initial capacitance after 2 billion galvanostatic charge/discharge cycles at high current density of 0.5 mA.cm-2 in an aqueous electrolyte of Na2SO4. In this manuscript we have also performed a comprehensive electrical study of the alumina/silicon interface which demonstrates that such nanometric layer of dielectric is not fully resistive as assumed by most the electrochemist but rather able to conduct electricity through tunnelling effect dependant on the thickness. Eventually we have used this conductive and protective layer to strengthen a pseudocapacitive conductive polymer which is electrochemically active in aqueous electrolytes. A promising composite material is described and realised by a simple drop-cast method of a PEDOT-PSS film onto silicon nanowires. The device exhibited promising performances with a specific energy of 2 Wh.kg-1 and a power density of 300 W.kg-1 at a current density of 1 A.g-1. The MSCs was able to retain 80% its initial capacitance after 500,000 galvanostatic charge-discharge cycles at 0.5 A.g-1. The last part of the thesis describes the collaboration sets with a Norvegian company, ELKEM SILICON MATERIALS, which has lead to the rethinking of our silicon nanostructure growing process and the large increase of the production capacity.
Ces dernières années, l’électronique portable connait un véritable essor, et envahit notre environnement. Le progrès technologique dans le domaine de la microélectronique a permis la réduction conséquente des dimensions des composants électroniques et ouvert des possibilités de mise en réseau et de contrôle jusqu’alors impossible. La question de l’alimentation en énergie est primordiale pour ces réseaux et leur déploiement n’est possible à condition de garantir leur autonomie énergétique. La production autonome d’énergie est souvent privilégiée pour que les microsystèmes soient capables de s’alimenter librement en énergie d’origine mécanique, thermique ou solaire. De telles sources de production restent intermittentes et c’est en miniaturisant les dispositifs de stockage que leur autonomie réelle leur sera envisageable. Pour répondre à ces besoins en sources d’énergie stables et miniaturisables, des micro-batteries ont été développées en parallèle des progrès conséquents du domaine des accumulateurs électrochimiques secondaires. Les micro-batteries souffrent néanmoins de limitations intrinsèques qui se voient exacerbées à échelle micrométrique. Elles se voient donc peu à peu remplacées ou combinées ces dernières années avec des unités de stockage de type supercondensateur désigné sous le terme « micro-supercondensateur » (souvent abrégé MSC) car utilisé à l’échelle microscopique. Ces travaux de thèse proposent de confronter une solution pour micro-supercondensateurs, les nanostructures de silicium aux nouveaux enjeux du stockage de l’énergie. Un état des lieux de la technologie sera tout d’abord proposé avec la mise en évidence de faiblesses majeures. Une étude électrique fondamentale permettra ensuite de comprendre le fonctionnement d’une protection électrochimique mise en place historiquement. Les nanostructures de silicium seront ensuite ouvertes au fonctionnement en électrolyte aqueux, l’une de leur faiblesse principale. Ces avancées permettront la résiliation d’un matériau composite capable de performances capacitives jamais atteintes pour un polymère conducteur. Enfin, la collaboration avec le groupe Elkem Silicon Materials permettra de préparer cette technologie aux nouveaux enjeux du stockage en micro-dispositifs avec l'augmentation substantive des capacités de production disponibles à l'échelle laboratoire.
Fichier principal
Vignette du fichier
VALERO_2020_diffusion.pdf (12.57 Mo) Télécharger le fichier
Origine : Version validée par le jury (STAR)

Dates et versions

tel-03555105 , version 1 (03-02-2022)

Identifiants

  • HAL Id : tel-03555105 , version 1

Citer

Anthony Valero. Fonctionnalisation d’électrodes de silicium nanostructuré par couches nanométriques de diélectrique par ALD : une protection active versatile pour des micro-supercondensateurs ultra-stables en milieux aqueux. Génie des procédés. Université Grenoble Alpes [2020-..], 2020. Français. ⟨NNT : 2020GRALI006⟩. ⟨tel-03555105⟩
147 Consultations
169 Téléchargements

Partager

Gmail Facebook X LinkedIn More